Peeled/Turned 0.75 High Speed Steel Round Bar, Sold in Lbs.

Part Number: 0.750M2-PB-11-LBS

Peeled/Turned High Speed Steel Round Bar Diameter: 0.75 Rockwell Hardness: 35-40 Annealing Temp: 1550F/1600F Preheat Temp: 1500F/1550F Austenitizing Temp: 2175F/2225F Quench Medium: Salt/Oil/Atm Tempering Temp: 1025F/1050F

California Residents

Prop 65 Warning: This product may contain chemicals known to the State of California to cause cancer, and birth defects or other reproductive harm.

$7.90

In Stock
Diameter

0.75

Rockwell Hardness

35-40

Annealing Temp

1550°F/1600°F

Preheat Temp

1500°F/1550°F

Austenitizing Temp

2175°F/2225°F

Quench Medium

Salt/Oil/Atm

Tempering Temp

1025°F/1050°F

Peeled/Turned 0.75 High Speed Steel Round Bar, Sold in Lbs.

Peeled/Turned 0.75 High Speed Steel Round Bar. This product is sold by the pound.

The main use of high-speed steels continues to be in the manufacture of various cutting tools. Typical applications for M2 high speed steel are twist drills, reamers, broaching tools, taps, milling tools, metal saws. M2 is suitable for cold forming tools such as extrusion rams and dies, also widely used in all kinds of cutting tools, knife and punches and die applications, plastic moulds with elevated wear resistance and screws.

M2 High Speed Steel is the “standard” and most widely used industrial High Speed Steel. It has small and evenly distributed carbides giving high wear resistance, though its decarburization sensitivity is a little bit high. After heat treatment, its hardness is the same as T1, but its bending strength can reach 4700 MPa, and its toughness and thermo-plasticity are higher than T1 by 50%. It is usually used to manufacture a variety of tools, such as drill bits, taps and reamers. 1.3343 is the equivalent numeric designation for M2 material identified in ISO 4957. Substantial savings are available for large quantity buys of High Speed Steel Round Bars from Bristol Machine Company.